CBT® 100
聚丁烯对苯二甲酸酯
Cyclics Corporation 

Technical Data

产品说明

CBT® 100 resin melts to a water-like viscosity when heated, then polymerizes into the engineering thermoplastic polybutylene terephthalate (PBT). CBT 100 resin has a processing temperature range between 190-240°C (370-460°F) and will be available in both one and two-part systems. This resin is formulated for compounding, injection molding, nanocomposites, rotational molding and as carrier resin for color and filler concentrates.

CBT 100 resin has a melt temperature of 180°C (356°F). It is supplied in pellet form and does not require grinding for most rotational molding applications.

总体

材料状态 • 已商用：当前有效   
供货地区 • 北美洲 • 欧洲  
性能特点 • 耐化学性良好 • 耐气候影响性能良好  
 • 耐酒精 • 耐碳氢化合物  
     
形式 • 颗粒料   
加工方法 • 滚塑成型 • 注射成型  
     
物理性能   额定值 单位制 测试方法 
比重   1.31g/cm³ ASTM D792 
收缩率 - 流动 (4.00 mm)   1.5% ASTM D955 
机械性能   额定值 单位制 测试方法 
拉伸模量   2700MPa ISO 527-2 
拉伸应力 (屈服)   54.0MPa ISO 527-2 
拉伸应变     
屈服   3.2% ISO 527-2 
断裂   50% ISO 527-2/5 
弯曲模量   2380MPa ISO 178 
弯曲强度   74.0MPa ISO 178 
冲击性能   额定值 单位制 测试方法 
悬壁梁缺口冲击强度 (23°C)   6.7kJ/m² ISO 180/1A 
无缺口伊佐德冲击强度 (23°C)   无断裂 ISO 180/1U 
热性能   额定值 单位制  
熔融温度   180°C  
可燃性   额定值 单位制 测试方法 
UL 阻燃等级 (4.00 mm)   HB UL 94 
充模分析   额定值 单位制 测试方法 
熔体密度   1.14g/cm³  
熔体粘度    ASTM D3835 
180°C, 10.0 sec^-1   0.0330Pa•s  
190°C, 10.0 sec^-1   0.0260Pa•s  
200°C, 10.0 sec^-1   0.0180Pa•s  
210°C, 10.0 sec^-1   0.0150Pa•s  
220°C, 10.0 sec^-1   0.0120Pa•s  
补充信息     
Solid Heat Capacity, ASTM E1269: 1.25 J/g.°C   
Liquid Heat Capacity, ASTM E1269, 180°C (356°F): 1.96 J/g.°C   
Heat of Melting, ASTM E793: 64 J/g     
     
注射   额定值 单位制  
加工（熔体）温度   230 到 260°C  
模具温度   190 到 200°C