医疗级COC, 医用包装, 光学性能, 防潮性

 

APEL™ APL6015T

环烯烃共聚物

 

Mitsui Chemicals, Inc.

 

Technical Data

 

产品说明

APEL is a cyclo olefin copolymer (COC) developed by Mitsui Chemicals using Ziegler polymerization technology. Integration of the performance of polyolefin resins and that of amorphous resins enables control of heat resistance and fluidity. With the highest refractive index among amorphous polyolefins, it is low in optical anisotropy and extremely low in birefringence. Proven applications in optical plastic lenses. Excellent moisture-proof properties, chemical resistance and non-attachment characteristics that make it applicable as a medical packaging material. APEL's versatile functions and superior characteristics create new potential for transparent materials.

 

Features:

• Optical characteristics

• Moisture-proofness

• Chemical resistance

• Dimensional stability

• Heat resistant stiffness

• Superior moldability

Applications:

• Medical packaging

总体

材料状态 • 已商用：当前有效

资料 1 • Technical Datasheet (English)

搜索 UL 黄卡 •  Mitsui Chemicals, Inc.

• APEL™

供货地区 • 亚太地区

• Good Heat Resistance • 光学性能 • 耐化学性良好

特性 • 尺寸稳定性良好 • 良好的成型性能

• 防潮性 • 良好刚性

用途 • 医用包装

加工方法 • 注射成型

 

物理性能 额定值(英制) 额定值(公制) 测试方法

密度 / 比重 1.04 1.04g/cm³ ASTM D792

熔流率（熔体流动速率） (260°C/2.16 kg) 10g/10 min 10g/10 min ASTM D1238

收缩率 内部方法

流动 6.0E-3in/in 0.60%

横向流动 5.0E-3in/in 0.50%

机械性能 额定值(英制) 额定值(公制) 测试方法

抗张强度 (屈服) 8700psi 60.0MPa ASTM D638

伸长率 (断裂) 3.0% 3.0% ASTM D638

弯曲模量 464000psi 3200MPa ASTM D790

弯曲强度 16000psi 110MPa ASTM D790

薄膜 额定值(英制) 额定值(公制) 测试方法

水气透过率 g•mil/ g•mm/m²/atm/24 ASTM F1249

0.23100in²/atm/24 hr 0.090hr

冲击性能 额定值(英制) 额定值(公制) 测试方法

悬壁梁缺口冲击强度 0.47ft•lb/in 25J/m ASTM D256

无缺口悬臂梁冲击 4.76ft•lb/in² 10.0kJ/m² ASTM D256

热性能 额定值(英制) 额定值(公制) 测试方法

载荷下热变形温度 (264 psi (1.8 MPa), 未退火) 275°F 135°C ASTM D648

玻璃转化温度 293°F 145°C 内部方法

线形热膨胀系数 ASTM D696

流动 3.9E-5in/in/°F 7.0E-5cm/cm/°C

横向 3.3E-5in/in/°F 6.0E-5cm/cm/°C

 

 

APEL™ APL6015T

环烯烃共聚物

Mitsui Chemicals, Inc.

光学性能 额定值 (英制) 额定值(公制) 测试方法

折射率 1.540 1.540 ASTM D542

透射率 90.0% 90.0% ASTM D1003

雾度 4.0% 4.0% ASTM D1003

注射 额定值(英制) 额定值(公制)

干燥温度 176 到 212°F 80 到 100°C

干燥时间 4.0 到 5.0hr 4.0 到 5.0hr

模具温度 < 284°F < 140°C

 

 

 