Vectra® MT1345 VF3001 (natural) is a 30% mineral filled, easy flow LCP grade for injection molding.

 

Vectra® MT1345 VF3001 (natural) is a special grade developed for medical industry applications and complies with:

 

• Food Contact Substance Notification (FCN) No. 742 of the Food and Drug Administration (FDA) and is listed in the Drug Master File (DMF 8464) and the Device Master File (MAF 315) 

• the corresponding EU and national registry regulatory requirements 

• biocompatibility in tests corresponding to USP 23 Class VI/ISO 10993 

• low residual monomers 

• no animal products 

 

Best overall surface appearance with properties similar to MT1310. Less abrasive than glass fiber reinforced grades. Improved toughness over MT1310. Outstanding hydrolytic stability. Recommended where aesthetics are key.

Chemical abbreviation according to ISO 1043-1 : LCP Inherently flame retardant.

总体

材料状态 • 已商用：当前有效

资料 1 • Technical Datasheet (English)

搜索 UL 黄卡 •  Celanese Corporation

•  Vectra®

供货地区 • 北美洲 • 拉丁美洲 • 亚太地区

• 非洲和中东 • 欧洲

填料/增强材料 • 矿物填料, 30% 填料按重量

• 良好的流动性 • 水解稳定 • 优良外观

特性 • 韧性良好 • 外观良好

• 阻燃性

• 食品接触的合规性 • 无动物源性成分

用途 • 医疗/护理用品

机构评级 • DMF 8464 • ISO 10993 • USP XXIII, Class VI

• FDA FCN 742 • MAF 315

RoHS 合规性 • 联系制造商

加工方法 • 注射成型

树脂 ID (ISO 1043) • LCP

物理性能 额定值(英制) 额定值(公制) 测试方法

密度 1.65g/cm³ 1.65g/cm³ ISO 1183

收缩率 ISO 294-4

横向流量 0.70% 0.70%

流量 0.20% 0.20%

机械性能 额定值(英制) 额定值(公制) 测试方法

拉伸模量 1.60E+6psi 11000MPa ISO 527-2/1A

拉伸应力 (断裂) 23200psi 160MPa ISO 527-2/1A/5

拉伸应变 (断裂) 4.6% 4.6% ISO 527-2/1A/5

弯曲模量 (73°F (23°C)) 1.73E+6psi 11900MPa ISO 178

弯曲应力 (73°F (23°C)) 26100psi 180MPa ISO 178

压缩模量 1.38E+6psi 9500MPa ISO 604

压缩应力 (1% 应变) 8700psi 60.0MPa ISO 604

冲击性能 额定值(英制) 额定值(公制) 测试方法

简支梁缺口冲击强度 (73°F (23°C)) 12ft•lb/in² 25kJ/m² ISO 179/1eA

简支梁无缺口冲击强度 (73°F (23°C)) 24ft•lb/in² 50kJ/m² ISO 179/1eU

悬壁梁缺口冲击强度 (73°F (23°C)) 13ft•lb/in² 27kJ/m² ISO 180/1A

无缺口伊佐德冲击强度 (73°F (23°C)) 19ft•lb/in² 40kJ/m² ISO 180/1U

硬度 额定值(英制) 额定值(公制) 测试方法

洛氏硬度 (M 计秤) 67 67 ISO 2039-2

 

Vectra® MT1345

液晶聚合物

 

Celanese Corporation

热性能 额定值(英制) 额定值(公制) 测试方法

热变形温度

66 psi (0.45 MPa), 未退火 397°F 203°C ISO 75-2/B

264 psi (1.8 MPa), 未退火 374°F 190°C ISO 75-2/A

1160 psi (8.0 MPa), 未退火 250°F 121°C ISO 75-2/C

维卡软化温度 304°F 151°C ISO 306/B50

熔融温度 3 536°F 280°C ISO 11357-3

线形热膨胀系数 ISO 11359-2

流动 5.6E-6in/in/°F 1.0E-5cm/cm/°C

横向 1.7E-5in/in/°F 3.0E-5cm/cm/°C

电气性能 额定值(英制) 额定值(公制) 测试方法

表面电阻率 > 1.0E+15ohms > 1.0E+15ohms IEC 60093

体积电阻率 1.0E+14ohms•cm 1.0E+14ohms•cm IEC 60093

介电强度 1100V/mil 44kV/mm IEC 60243-1

相对电容率 IEC 60250

100 Hz 3.80 3.80

1 MHz 3.20 3.20

耗散因数 IEC 60250

100 Hz 0.010 0.010

1 MHz 0.016 0.016

耐电弧性 180sec 180sec 内部方法

漏电起痕指数 200V 200V IEC 60112

可燃性 额定值(英制) 额定值(公制) 测试方法

UL 阻燃等级 V-0 V-0 UL 94

注射 额定值(英制) 额定值(公制)

干燥温度 302°F 150°C

干燥时间 4.0 到 6.0hr 4.0 到 6.0hr

建议的最大水分含量 0.010% 0.010%

料斗温度 68 到 86°F 20 到 30°C

料筒后部温度 518 到 536°F 270 到 280°C

料筒中部温度 527 到 545°F 275 到 285°C

料筒前部温度 536 到 554°F 280 到 290°C

射嘴温度 554 到 572°F 290 到 300°C

加工（熔体）温度 545 到 563°F 285 到 295°C

模具温度 176 到 248°F 80 到 120°C

注射速度 快速 快速

背压 < 435psi < 3.00MPa

注射说明

Feeding zone temperature: 60 to 80°C

Zone4 temperature: 285 to 295°C

Hot runner temperature: 285 to 295°C

 

 

 

 