医疗级LDPE, FDA食品级，HPFB (加拿大) No Objection

 

陶氏低密度聚乙烯 310E

Low Density Polyethylene Resin

陶氏塑料

Technical Data

 

产品说明

DOW LDPE 310E is a fractional melt index low density polyethylene resin. DOW LDPE 310E has been specially designed for superior processability on blown film lines leading to significant output improvements. The resin offers additionally excellent draw down. It can be used pure or in blends with LLDPE resins.

 

Applications:

• lamination film, shrink film, and stretch film

 

Main Characteristics:

• Excellent processability and draw down 

• Good physical properties in blends with LLDPE 

• Can be readily extruded using conventional blown film techniques at melt temperatures between 160 and 195°C 

 

Complies with:

• U.S. FDA 21 CFR 177.1520 ( c )2.2 

• EU, No 10/2011 

• U.S. FDA-DMF 

• Canadian HPFB No Objection 

 

Consult the regulations for complete details.

 

Slip Additive: 0 ppm

Antiblock Additive: 0 ppm

总体

材料状态 • 已商用：当前有效

资料 1 • Technical Datasheet

搜索 UL 黄卡 •  陶氏塑料

供货地区 • 欧洲 • 亚太地区

机构评级 • DMF 未评级 • HPFB (加拿大) No Objection

• FDA 21 CFR 177.1520(c) 2.2 • 欧洲 No 10/2011

形式 • 粒子

 

物理性能 额定值(英制) 额定值(公制) 测试方法

密度 / 比重 0.925 0.923g/cm³ ASTM D792

熔流率（熔体流动速率） (190°C/2.16 kg) 0.75g/10 min 0.75g/10 min ASTM D1238

机械性能 额定值(英制) 额定值(公制) 测试方法

摩擦系数 0.50 到 0.70 0.50 到 0.70 ASTM D1894

薄膜 额定值(英制) 额定值(公制) 测试方法

薄膜厚度 - 经测试 2.0mil 50µm

膜刺穿强度 (2.0 mil (50 µm)) 15.9in•lb 1.80J 内部方法

膜刺穿力 (2.0 mil (50 µm)) 11.2lbf 50.0N 内部方法

膜耐刺穿性 (2.0 mil (50 µm)) 48.3ft•lb/in³ 4.00J/cm³ 内部方法

割线模量 ASTM D882

2% 正割, MD : 2.0 mil (50 µm), 吹塑薄膜 25400psi 175MPa

2% 正割, TD : 2.0 mil (50 µm), 吹塑薄膜 26800psi 185MPa

抗张强度 ASTM D882

MD : 屈服, 2.0 mil (50 µm), 吹塑薄膜 1600psi 11.0MPa

TD : 屈服, 2.0 mil (50 µm), 吹塑薄膜 1600psi 11.0MPa

MD : 断裂, 2.0 mil (50 µm), 吹塑薄膜 3630psi 25.0MPa

TD : 断裂, 2.0 mil (50 µm), 吹塑薄膜 3340psi 23.0MPa

伸长率 ASTM D882

MD : 断裂, 2.0 mil (50 µm), 吹塑薄膜 390% 390%

TD : 断裂, 2.0 mil (50 µm), 吹塑薄膜 570% 570%

落锤冲击 (2.0 mil (50 µm), 吹塑薄膜) 170g 170g ASTM D1709A

 

陶氏低密度聚乙烯 310E

Low Density Polyethylene Resin

 

陶氏塑料

薄膜 额定值(英制) 额定值(公制) 测试方法

埃尔曼多夫抗撕强度 3 ASTM D1922

MD : 2.0 mil (50 µm), 吹塑薄膜 350g 350g

TD : 2.0 mil (50 µm), 吹塑薄膜 260g 260g

光学性能 额定值(英制) 额定值(公制) 测试方法

光泽度 (45°, 1.97 mil (50.0 µm), 吹塑薄膜) 58 58 ASTM D2457

雾度 (1.97 mil (50.0 µm), 吹塑薄膜) 9.2% 9.2% ASTM D1003

挤出 额定值(英制) 额定值(公制)

熔体温度 320 到 383°F 160 到 195°C

挤压说明

吹塑薄膜的制造条件：

• 螺杆类型：通用

• 输出：25 kg/h

• 模具直径：150 mm。

• 放大比：2.5

• 螺杆速度：77 rpm

 

备注

1 通过这些链接您能够访问供应商资料。我们尽量保证及时更新资料；不过您可以从供应商处了解最新资料。

2 一般属性：这些不能被视为规格。

 

3 方法 B

 

 

 

 

 

医疗级LDPE塑胶原料,医疗级低密度聚乙烯塑胶原料， 医疗级LDPE 陶氏低密度聚乙烯 310E是东莞市双帮塑胶原料有限公司常年销售的塑料，因为塑料价格行情每天都有新变化前天的报价不等于今天的报价。本公司销售的所有原料保证是原厂原包,随料可以提供生产厂商提供的物性表、SGS报告，COA原料出厂报告,REACH报告,SVHC报告,UL黄卡,提供原料注塑加工工程中可能出现的各种异常现象解决方法，塑料牌号太多，本网站没有提供的本公司也有代理，详情请咨询本公司相关业务人员0769-87795123   13549213581 肖生    QQ：15397858   微信：13549213581