医疗级PEEK, ISO 10993

 

KetaSpire® KT-820FP

聚醚醚酮

Solvay Specialty Polymers

Technical Data

 

产品说明

KetaSpire® KT-820FP is the low-flow grade of unreinforced polyetheretherketone (PEEK) supplied in a natural-color fine powder form suitable for compression molding.

 

KetaSpire® PEEK is produced to the highest industry standards and is characterized by a distinct combination of properties, which include excellent wear resistance, best-in-class fatigue resistance, ease of melt processing, high purity, and excellent chemical resistance to organics, acids, and bases.

 

These properties make it well-suited for applications in healthcare, transportation, electronics, chemical processing, and other industrial uses.

 

The resin is also available as KetaSpire® KT-820 NT in a natural-color pellet form for injection molding and extrusion.

 

总体

 

材料状态

 

 

资料 1

 

搜索 UL 黄卡

 

供货地区

 

特性

 

用途

 

机构评级

 

RoHS 合规性 外观 形式 加工方法

 

 

 

 

 

• 拉丁美洲 • 亚太地区

• 欧洲

• 耐疲劳性能 • 阻燃性

• 耐热性，高

• 延展性

• 工业应用 • 石油/天然气用品

 

 

物理性能 额定值(英制) 额定值(公制) 测试方法

密度 / 比重 1.30 1.30g/cm³ ASTM D792

熔流率（熔体流动速率） (400°C/2.16 kg) 3.0g/10 min 3.0g/10 min ASTM D1238

吸水率 (24 hr) 0.10% 0.10% ASTM D570

颗粒大小

保留在 100 目的筛网上 < 0.00% < 0.00%

保留在 140 目的筛网上 < 2.00% < 2.00%

机械性能 额定值(英制) 额定值(公制) 测试方法

拉伸模量 530000psi 3650MPa ASTM D638

抗张强度 14000psi 96.5MPa ASTM D638

伸长率 ASTM D638

屈服 5.2% 5.2%

断裂 3 > 60% > 60%

断裂 4 20 到 30% 20 到 30%

弯曲模量 560000psi 3860MPa ASTM D790

弯曲强度 22000psi 152MPa ASTM D790

冲击性能 额定值(英制) 额定值(公制) 测试方法

悬壁梁缺口冲击强度 1.3ft•lb/in 69J/m ASTM D256

无缺口悬臂梁冲击 无断裂 无断裂 ASTM D256

热性能 额定值(英制) 额定值(公制) 测试方法

载荷下热变形温度 (264 psi (1.8 MPa), 未退火) 324°F 162°C ASTM D648

玻璃转化温度 302°F 150°C ASTM D3417

熔融温度 644°F 340°C ASTM D3417

线形热膨胀系数 - 流动 2.4E-5in/in/°F 4.3E-5cm/cm/°C ASTM E831

(-58 到 122°F (-50 到 50°C))

 

KetaSpire® KT-820FP

聚醚醚酮

Solvay Specialty Polymers

充模分析 额定值(英制) 额定值(公制) 测试方法

熔体粘度 (752°F (400°C), 1000 sec^-1) 420Pa•s 420Pa•s ASTM D3835