医疗级PPO, 医疗/护理用品, 无溴阻燃

 

NORYL™ Resin FNH2160 - Americas

聚苯醚 + PS

SABIC

Technical Data

 

Product Description

Non brominated non chlorinated flame retarded NORYL resin for structural foam applications. 80C HDT. All values at 20% weight reduction.

General

Material Status • 已商用：当前有效

资料 1 • Technical Datasheet

UL 黄卡 2 • E121562-101920328

搜索 UL 黄卡 • SABIC

• NORYL™ Resin

Availability • 北美洲 • 拉丁美洲

Additive • 阻燃性

Features • Chlorine Free • 无溴

• 可发泡性能 • 阻燃性

Uses • 医疗/护理用品

Processing Method • 泡沫处理

Also Available In • Asia Pacific • Europe

Physical 额定值(英制) 额定值(公制) 测试方法

Density / Specific Gravity ASTM D792

-- 4 0.880 0.878g/cm³

-- 1.12 1.12g/cm³

Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) 2.20in³/10min 36.0cm³/10min ISO 1133

Molding Shrinkage - 流动 (0.252 in (6.40 mm)) 5.0E-3 到 8.0E-3in/in 0.50 到 0.80% Internal Method

Water Absorption (24 hr) 0.070% 0.070% ASTM D570

Mechanical 额定值(英制) 额定值(公制) 测试方法

Tensile Strength ASTM D638

屈服, 0.250 in (6.35 mm) 5220psi 36.0MPa

断裂, 0.250 in (6.35 mm) 4930psi 34.0MPa

Tensile Elongation (断裂, 0.250 in (6.35 mm)) 12% 12% ASTM D638

Flexural Modulus (0.252 in (6.40 mm)) 326000psi 2250MPa ASTM D790

Flexural Strength (屈服, 0.252 in (6.40 mm)) 10200psi 70.0MPa ASTM D790

Impact 额定值(英制) 额定值(公制) 测试方法

Unnotched Izod Impact ASTM D4812

73°F (23°C), 0.252 in (6.40 mm) 6.8ft•lb/in 360J/m

Instrumented Dart Impact ASTM D3763

73°F (23°C), Energy at Peak 257in•lb 29.0J

Thermal 额定值(英制) 额定值(公制) 测试方法

Deflection Temperature Under Load ASTM D648

66 psi (0.45 MPa), 未退火, 0.252 in (6.40 mm) 199°F 93.0°C

264 psi (1.8 MPa), 未退火, 0.252 in (6.40 mm) 180°F 82.0°C

RTI Elec 149°F 65.0°C UL 746

RTI Imp 149°F 65.0°C UL 746

RTI Str 149°F 65.0°C UL 746

Flammability 额定值(英制) 额定值(公制) 测试方法

Flame Rating UL 94

0.12 in (3.0 mm) V-1 V-1

0.24 in (6.0 mm) V-0 V-0

0.15 in (3.9 mm) 5VA 5VA

Flame Class Minimum Density - Foam 53.06lb/ft³ 850kg/m³

 

NORYL™ Resin FNH2160 - Americas

聚苯醚 + PS

 

SABIC

Additional Information 额定值(英制) 额定值(公制)

Weight Reduction

Foam - Impact : 0.25 in (6.40 mm) 20% 20%

Foam - Mechanical : 0.25 in (6.40 mm) 20% 20%

Foam - Physical : 0.25 in (6.40 mm) 20% 20%

Foam - Thermal : 0.25 in (6.40 mm) 20% 20%

 

Injection Notes

Structural Foam Molding Parameters

• Blowing Agent, Physical System: Nitrogen Gas 

• Concentration Range (Blowing Agent): 1 to 3% 

• Recommended Concentration (Blowing Agent): 2% 

• Drying Temperature (Resin): 70 to 80°C 

• Drying Time (Resin): 2 to 4hrs 

• Drying Time (Resin, Cumulative): 8hrs 

• Melt Temperature: 270 to 310°C 

• Nozzle Temperature: 270 to 305°C 

• Front Temperature: 270 to 305°C 

• Middle Temperature: 270 to 305°C 

• Rear Temperature: 230 to 260°C 

• Mold Temperature: 25 to 55°C 

 

 

 

 

 

医疗级PPO原料,医疗级聚苯醚 + PS塑胶原料,医疗级PPO NORYL™ Resin FNH2160 - Americas是东莞市双帮塑胶原料有限公司常年销售的塑料，因为塑料价格行情每天都有新变化前天的报价不等于今天的报价。本公司销售的所有原料保证是原厂原包,随料可以提供生产厂商提供的物性表、SGS报告，COA原料出厂报告,REACH报告,SVHC报告,UL黄卡,提供原料注塑加工工程中可能出现的各种异常现象解决方法，塑料牌号太多，本网站没有提供的本公司也有代理，详情请咨询本公司相关业务人员0769-87795123   13549213581 肖生    QQ：15397858   微信：13549213581