医疗级TPE 95A, 医疗/护理用品, 薄膜, 包装, 药品包装, 医用包装, 薄膜挤出, 挤出吹塑成型

 

Ecdel™ 9965

热塑性弹性体

Eastman Chemical Company

Technical Data

 

产品说明

 

Ecdel™ elastomers are medical grade copolyester ethers (COPE). They offer the clarity, toughness, and chemical resistance needed in a variety of flexible packaging including medical applications. Ecdel™ Elastomer 9965 may be injection molded or extruded. Ecdel™ elastomers may be extrusion blow molded directly into bags or extruded into film for later fabrication into bags.

 

This product has been CRADLE TO CRADLE CERTIFIED Silver.

The CRADLE TO CRADLE CERTIFIED Mark is a registered certification mark used under license through McDonough Braungart Design Chemistry (MBDC). MBDC is a global sustainability consulting and product certification firm. The CRADLE TO CRADLE® framework moves beyond the traditional goal of reducing the negative impacts of commerce ('eco-efficiency'), to a new paradigm of increasing its positive impacts ('eco-effectiveness'). At its core, Cradle to Cradle design perceives the safe and productive processes of nature's 'biological metabolism' as a model for developing a 'technical metabolism' flow of industrial materials. Product components can be designed for continuous recovery and reutilization as biological and technical nutrients within these metabolisms. For more information about MBDC and to obtain printable certificates for Eastman Copolyesters, visit www.mbdc.com. Choose Eastman Chemical Company under Company Name in C2C Certified products to display a list of our products.

 

总体

 

材料状态 • 已商用：当前有效

资料 1 •  Technical Datasheet (English)

搜索 UL 黄卡 •  Eastman Chemical Company

供货地区 • 北美洲 • 拉丁美洲 • 欧洲

• 非洲和中东 • 南美洲 • 亚太地区

• 低萃取物 • 耐化学性良好 • 中等透明度

性能特点 • 良好的柔韧性 • 耐热性，高

• 良好杀的菌性 • 韧性良好

• 包装 • 管道 • 医用包装

用途 • 薄膜 • 药品包装

• 袋子 • 医疗/护理领域的应用

形式 • 颗粒料

加工方法 • 薄膜挤出 • 挤出吹塑成型

• 挤出 • 注射成型

物理性能 额定值单位制 测试方法

比重 1.13g/cm³ ASTM D792

熔流率 (230°C/2.16 kg) 20g/10 min ASTM D1238

吸水率 (23°C, 24 hr) 0.35% ASTM D570

固有粘度 3 (23°C) 1.1 Internal Method

机械性能 额定值单位制 测试方法

拉伸模量 (23°C) 170MPa ASTM D638

抗张强度 ASTM D638

屈服, 23°C, 3.00 mm, 注塑 4 14.0MPa

断裂, 23°C, 2.00 mm 5 20.0MPa

伸长率 ASTM D638

屈服, 23°C 30%

断裂, 23°C 300%

弯曲模量 (23°C) 150MPa ASTM D790

摩擦系数 > 1.0 ASTM D1894

薄膜 额定值单位制 测试方法

薄膜厚度 - 经测试 130µm

割线模量 ASTM D882

正切, MD: 130 µm 185MPa

正切, TD: 130 µm 179MPa

 

Ecdel™ 9965

热塑性弹性体

Eastman Chemical Company

薄膜 额定值单位制 测试方法

抗张强度 ASTM D882

MD: 屈服, 130 µm 13.7MPa

TD: 屈服, 130 µm 13.5MPa

MD: 断裂, 130 µm 23.7MPa

TD: 断裂, 130 µm 22.6MPa

伸长率 ASTM D882

MD: 屈服, 130 µm 26%

TD: 屈服, 130 µm 26%

MD: 断裂, 130 µm 550%

TD: 断裂, 130 µm 550%

透氧率 (30°C, 130 µm) 841cm³/m²/24 hr ASTM D1434

水气透过率 (38°C, 130 µm, 100% RH) 130g/m²/24 hr ASTM F372

弹性体 额定值单位制 测试方法

卡-伯模量 ASTM D1043

-70°C 930MPa

-28°C 240MPa

冲击性能 额定值单位制 测试方法

悬壁梁缺口冲击强度 (-40°C) 50J/m ASTM D256

硬度 额定值单位制 测试方法

硬度计硬度 ASTM D2240

邵氏 A, 23°C 95

邵氏 D, 23°C 55

热性能 额定值单位制 测试方法

脆化温度 < -75.0°C ASTM D746

玻璃转化温度(DSC) -3.00°C DSC

维卡软化温度 170°C ASTM D1525 6

熔融峰值温度 207°C ASTM D3418

结晶峰温 (DSC) 140°C DSC

线形膨胀系数 - 流动 (23°C) 0.000090cm/cm/°C ASTM D696

比热 DSC

25°C 7 1600J/kg/°C

100°C 7 1800J/kg/°C

150°C 7 2000J/kg/°C

175°C 7 2300J/kg/°C

200°C 8 3100J/kg/°C

225°C 9 2300J/kg/°C

导热系数 (23°C) 0.19W/m/K ASTM C177

融合热量 (23°C) 27.0kJ/kg ASTM E793

光学性能 额定值单位制 测试方法

光泽度 (45°, 130 µm) 80 ASTM D2457

透射率 ASTM D1003

总计, 130 µm 93.0%

常规, 130 µm 90.0%

雾度 (130 µm) 1.0% ASTM D1003

补充信息 额定值单位制 测试方法

Tear Strength (23°C) 370N ASTM D1004

 

 

 

 

 

 

医疗级热塑性弹性体TPE,医疗级塑胶原料TPE Ecdel™ 9965是东莞市双帮塑胶原料有限公司常年销售的塑料，因为塑料价格行情每天都有新变化前天的报价不等于今天的报价。本公司销售的所有原料保证是原厂原包,随料可以提供生产厂商提供的物性表、SGS报告，COA原料出厂报告,REACH报告,SVHC报告,UL黄卡,提供原料注塑加工工程中可能出现的各种异常现象解决方法，塑料牌号太多，本网站没有提供的本公司也有代理，详情请咨询本公司相关业务人员0769-87795123 